布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
HRA | HRC | HRA | HRC | ||||
86.6 | 70.0 | 1037 | 78.5 | 55.0 | 599 | ||
86.3 | 69.5 | 1017 | 78.2 | 54.5 | 589 | ||
86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
84.7 | 66.5 | 906 | 76.6 | 51.5 | 534 | ||
84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 |
የብረታ ብረት ቁሳቁሶች ጥንካሬ እሴት የመቀየሪያ ሰንጠረዥ
布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
HRA | HRC | HRA | HRC | ||||
370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
273 | 28.5 | 278 |
ማስታወሻ፡-
1. ብሬንል ጠንካራነት፡- በዋናነት የ castings፣ forgings፣ iron non-ferrous የብረት ክፍሎች፣ ትኩስ-ጥቅል-ቢሌቶች እና annealed ክፍሎች ጠንካራነት ለመለካት ጥቅም ላይ ይውላል። የመለኪያ ክልል ≥HB450 ነው።
2. የሮክዌል ጠንካራነት፡ HRA በዋናነት ለከፍተኛ ጠንካራነት ናሙናዎች የሚውለው የቁሳቁሶች እና የወለል ንጣፎች ጥንካሬ ከኤችአርሲ67 ከፍ ያለ ጥንካሬ ያላቸው እንደ ሲሚንቶ የተሰራ ካርባይድ፣ ናይትራይድ ብረት ወዘተ የመሳሰሉትን ለመለካት ነው። የመለኪያ ክልሉ HRA>70 ነው። ኤችአርሲ በዋናነት የብረት ክፍሎችን (እንደ የካርቦን ብረት ፣ የመሳሪያ ብረት ፣ ቅይጥ ብረት ፣ ወዘተ) ከመጥፋት ወይም ከሙቀት በኋላ ጥንካሬን ለመለካት ጥቅም ላይ ይውላል። የመለኪያ ክልሉ HRC20 ~ 67 ነው።
3. ቪከርስ ጠንካራነት፡- የቀጭን ክፍሎችን እና የብረት ሳህን ክፍሎችን ጥንካሬን ለመለካት የሚያገለግል ሲሆን እንደ ካርቡሪዚንግ፣ ሳይያኒዲንግ እና ናይትራይዲንግ ያሉ የገጽታ ጠንከር ያሉ ክፍሎችን ጥንካሬ ለመለካት ይጠቅማል።